PENGARUH MASSA BENTONIT TERAKTIVASI H2SO4 TERHADAP DAYA ADSORPSI IODIUM (A STUDY OF INFLUENCE THE MASS ACTIVATED BENTONITE H2SO4 ON THE ADSORPTION OF IODINE)

Abstract

Abstrak. Telah dilakukan penelitian tentang pengaruh massa bentonit teraktivasi H₂SO₄ terhadap daya adsorpsi iodium. Tujuan dari penelitian ini untuk mengetahui karakteristik bentonit teraktivasi H₂SO₄, serta untuk mengetahui pengaruh massa bentonit teraktivasi H₂SO₄ terhadap daya adsorpsi iodium. Karakteristik bentonit teraktivasi H₂SO₄ diuji dengan spektrofotometer infra merah, difraktometer sinar-X, scanning electron microscopy, dan surface area anlyzer. Untuk mengetahui pengaruh massa bentonit teraktivasi H₂SO₄ terhadap daya adsorpsi iodium dilakukan dengan metode titrasi iodometri. Hasil penelitian menunjukkan bahwa karakteristik bentonit aktif mempunyai gugus fungsional khas pada bilangan gelombang 1038,9 cm^-1 yang merupakan regangan asimetris Si-O-Si, bilangan gelombang 921,2 cm^-1 merupakan regangan Al-O-Al, dan bilangan gelombang 786,2 cm^-1 yang merupakan vibrasi tekuk Al-O-Al_. Sedangkan komposisi kimianya adalah Montmorillonit, Quartz dan Halloysite. Analisis menggunakan scanning electron microscopy menunjukkan adanya perubahan pori pada bentonit aktif menjadi lebih bersih dan halus serta pori-pori menjadi lebih besar. Hasil analisis menggunakan surface area anlyzer menunjukkan adanya peningkatan luas permukaan, volume total pori, dan rata-rata jari pori menjadi 90,718 (m²/g), 150,4 x 10^-3 (ml/g), dan 33,1567 . Semakin banyak jumlah adsorben yang digunakan untuk proses adsorpsi iodium, maka semakin besar persentase iodium yang teradsorpsi. Persen adsorpsi terjadi pada penggunaan bentonit sebanyak 7 % yaitu sebesar 58,995 %.

Kata kunci: adsorpsi, bentonit teraktivasi, iodium.

Abstract. A study of influence the mass activated bentonite H₂SO₄ on the adsorption of iodine has done research. The purpose of this study to investigate the characteristics of activated bentonite H₂SO₄, and to investigate the effect of mass activated bentonite H₂SO₄ on the adsorption of iodine. Characteristics of activated bentonite H2SO4 tested with Infra Red spectrophotometer, X-ray diffractometer, scanning electron microscopy, and surface area anlyzer. To determine the effect of mass activated bentonite H₂SO₄ on the adsorption of iodine carried by iodometric titration method. The results showed that the characteristics of active bentonite has the typical functional group at wavenumber 1038,9 cm^-1 which is the asymmetric stretch of Si-O-Si, the wavenumber 921,2 cm^-1 is astrain O-Al-O,  and the wavenumber 786,2 cm^-1 which is bend vibration of Al-O-Al. While the chemical composition is montmorillonite, Quartz and Halloysite. Analysis using scanning electron microscopy showed changes in the avtivated bentonite, the pores become more numerous and larger, and the release of impurities on the surface of bentonite. Results of analysis using the surface area anlyzer showed an increase in surface area, total pore volume, and average pore size becomes 90,718 (m²/g), 150,4. 10^-3 (ml/g), and 33,1567 Å. The more of adsorbent bentonite from is used for iodine adsorption process, the greater percentage of adsorbed iodine. Percent adsorption occurs on the use 7% of bentonite is 58,995%.

Keywords: adsorption, activated bentonite, iodine.