KAPASITAS ADSORPSI SILIKA ABU SEKAM PADI TERMODIFIKASI ARGININ UNTUK ADSORPSI ION LOGAM Cr(VI) ADSORPSION CAPACITY OF RICE HUSK ASH SILICA OF ARGININE MODIFIED FOR ADSORPTION Cr(VI) METAL ION

  • DIAN AYU WULANDARI

Abstract

Abstrak. Silika yang terbuat dari abu sekam padi dengan penambahan asam sitrat telah berhasil dimodifikasi menggunakan arginin dan senyawa penghubung 3-glisidoksipropiltrimetoksisilan (GPTMS). Modifikasi silika abu sekam padi (SGASP) dilakukan menggunakan metode sol gel. Tujuan penelitian ini untuk mengetahui gugus fungsional adsorben silika abu sekam padi yang telah termodifikasi arginin (SASPArg), pengaruh pH, dan kapasitas adsorpsinya terhadap ion logam Cr(VI). Karakterisasi gugus fungsional dilakukan menggunakan teknik spektofotometri inframerah, kemampuan adsorben dengan pengaruh  pH  dan konsentrasi  dilakukan dalam sistem batch. Kadar ion logam Cr(VI) dalam larutan diukur dengan teknik Spektrofotometri Serapan Atom. Kapasitas adsorpsi dianalisis dengan model isotherm adsorpsi Langmuir dan Freundlich. Hasil karakterisasi inframerah (FTIR) dari SGASP menunjukkan munculnya pita pada daerah 3435,91 cm-1 yang merupakan vibrasi gugus OH dari silanol. Adanya bilangan gelombang pada 3431,07 cm-1, 1651,57 cm-1 dan 1400,41 cm-1  menunjukkan vibrasi ulur N-H, C=N, dan COO dari arginin serta hilangnya bilangan gelombang pada 910,01 cm-1 yang merupakan vibrasi cincin epoksida dari GPTMS menandakan SASPArg telah terbentuk.  Aplikasi SASPArg dan SGASP untuk adsorpsi ion logam Cr(VI) terjadi maksimum masing- masing pada pH 2 dan 6,  sebesar 77,17%  dan 16,89% . Kapasitas adsorpsi menggunakan model isoterm adsorpsi Langmuir pada SASPArg dan SGASP berturut-turut sebesar 4,64x10-4 mol/g dan 1,74x10-4 mol/g, sedangkan dengan model isoterm Freundlich sebesar 2,20x10-2 mol/g dan 1,98x10-2 mol/g.

Kata kunci: silika abu sekam padi, arginin, 3-glisidoksipropiltrimetoksisilan, kapasitas adsorpsi, Cr(VI).

 

Abstract.. Silica was made from rice husks ash with added citric acid, modified with the amino acid arginine and coupling agent of 3-glycidoxypropyltrimethoxysilane (GPTMS) was successfully done. The modification of rice husks ash silica (SGASP) has been done by using sol gel method. The purpose of this research was to cognize functional group of adsorbent rice husk ash silica was modified with amino acid arginine (SASPArg),  pH effect, and his adsorption capacity to Cr(VI) metal ion. The characterization of functional group was determined by using infrared spectrophotometry technique (FTIR), while capability of adsorbent with pH effect and concentration conducted in bath system. The trace of Cr(VI) metal ion in aqueous solution measured by atomic absorption spectrophotometry technique. Adsorption capacity analyzed by Langmuir and Freundlich isotherm adsorption model. The result of this research obtained a peak on 3435,91 cm-1, showing stretching vibration OH from silanol in SGASP. The peak on 3431,07 cm-1, 1651,57 cm-1 and 1400,41 cm-1 that showed stretching  vibration of  N-H, C=N, and COO  from arginine and also lost of peak on 910,01 cm-1 from epoxide ring vibration on GPTMS indicated that SASPArg adsorbent has been formed. Applications of SASPArg and SGASP for adsorption Cr(VI) metal ions took place maximum at pH 2 and 6 was 77,17% and 16,89%. The adsorption capacity using Langmuir isoterm adsorption model of SASPArg and SGASP was obtained 4,64x10-4 mol/g and 1,74x10-4 mol/g, while Freundlich was obtained 2,20x10-2 mol/g dan 1,98x10-2 mol/g.

Keywords: silica rice husk ash, arginine, 3-glycidoxypropyltrimethoxysilane, adsorption capacity, Cr(VI).

Published
2015-01-31
Abstract View: 6
PDF Download: 50