SINTESIS DAN KARAKTERISASI HIDROKSIAPATIT DARI CANGKANG KEPITING (scylla serrata) DENGAN METODE PENGENDAPAN BASAH SYNTHESIS AND CHARACTERIZATION OF HYDROXYAPATITE OF CRABS SHELL (scylla serrata) BY WET APPLICATION METHOD

  • DICKY SUPANGAT

Abstract

Abstrak. Hidroksiapatit dapat disintesis dengan sumber kalsium berasal dari cangkang kepiting dengan metode penambahasan fosfat secara single drop. Cangkang kepiting yang dikalsinasi pada suhu 1000 oC selama 5 jam dari hasil analisis menggunakan XRD menghasilkan fasa utama berupa Ca(OH)­2. Larutan H3PO4 ditambahkan kedalam larutan (CaOH)2 secara single drop. Dilakukan aging selama 24 jam dan digunakan suhu sintering 900oC selama 2 jam. Hasil sintesis dikarakterisasi menggunakan XRD menghasilkan fasa utama berupa hidroksiapatit dengan kristanilitas sebesar 83.98%. Analisis dengan FTIR menunjukan gugus utama hiroksiapatit hasil sintesis berupa PO43-. Analisis dengan SAA menunjukan luas permukaan hidroksiapatit sebesar 0,50 m2/g, ukuran pori sebesar 123,20 nm, dan volume pori sebesar 31,02 mm3/g. Analisis dengan SEM menunjukan morfologi hidrosiapatit berupa bongkahan dengan pori yang tersebar merata dan hasil uji tekan menunjukan kekauatan tekan Hidroksiapatit sebesar 56,92 Mpa.

Kata Kunci: hidroksiapatit, cangkang kepiting,  single drop.

 

Abstract. Hydroxyapatite can be synthesized with a calcium source derived from a crab shell with a single drop phosphate method. The calcined crab shell at 1000 oC for 5 hours from the analysis using XRD resulted in the main phase of Ca (OH)2. H3PO4 solution is added to solution (CaOH) 2 in single drop. Conducted aging for 24 hours and used sintering temperature 900 oC for 2 hours. The synthesized results were characterized using XRD resulting in a hydroxyapatite main phase with crystallinity of 83.98%. The analysis with FTIR shows the main hieroxyapatite group of synthesized form of PO43-. Analysis with SAA showed a hydroxyapatite surface area of ​​0.50 m2 / g, a pore size of 123.20 nm, and a pore volume of 31.02 mm3/ g. The analysis with SEM shows the hydroxyapatite morphology in the form of chunks with uniformly distributed pores and the result of the compressive test shows a hydroxyapatite compressive strength of 56.92 MPa.

Key words: hydroxyapatite, crab shell, single drop.

Published
2017-10-11
Abstract View: 13
PDF Download: 239