PEMANFAATAN MEMBRAN KITOSAN-SILIKA UNTUK MENURUNKAN KADAR ION LOGAM PB(II) DALAM LARUTAN (UTILIZATION OF CHITOSAN-SILICA TO REDUCE PB(II) ION LEVELS IN SOLUTION)

  • SHOFIYAH YUNIANTI Jurusan Kimia FMIPA Universitas Negeri Surabaya

Abstract

Abstrak. Telah dilakukan penelitian tentang pemanfaatan membran kitosan-silika untuk menurunkan kadar ion logam Pb(II) dalam larutan. Tujuan dari penelitian ini adalah untuk mengetahui karakteristik membran kitosan-silika dan kinerja membran untuk menyaring ion logam Pb(II) dalam larutan Pb(NO3)2. Membran kitosan-silika dibuat dengan variasi konsentrasi kitosan 0,25%; 0,5%; 1%; 2%; 3% dan konsentrasi silika 0,004 M.. Uji karakteristik membran meliputi uji swelling, uji sifat mekanik, uji morfologi membran, dan analisa gugus fungsi. Uji kinerja membran terhadap ion Pb(II) dilakukan dengan proses filtrasi larutan Pb(NO3. Dari hasil uji swelling dan uji sifat mekanik didapatkan membran yang memiliki karakteristik terbaik yaitu membran kitosan-silika 3% Analisa gugus fungsi menunjukkan bahwa membran kitosan-silika 3% mengalami pergeseran, penurunan atau peningkatan bilangan gelombang, serta ditemukan gugus fungsional baru yang menunjukkan adanya gugus silika pada membran. Membran kitosan-silika 3% mampu menyaring ion logam Pb(II) dengan koefisien rejeksi paling besar yaitu 26,84%. Analisa SEM secara umum menunjukkan bahwa membran kitosan-silika mempunyai morfologi permukaan yang rapat dan halus.

Kata kunci: membran kitosan-silika, filtrasi, ion logam Pb(II), koefisien rejeksi

Abstract. The study about utilization of chitosan-silica membranes to reduce Pb(II) ion levels in solution has been done. The purpose of this study was to determine the characteristics of chitosan-silica membrane and its performance to filter out the Pb(II) ion in solution of Pb(NO3)2. Chitosan-silica membranes were prepared by varying concentration of chitosan 0.25%, 0.5%, 1%, 2%, 3% and the silica concentration 0.004 M. The characteristics of membrane were analized by swelling test, mechanical test, morphology test, and functional group test. The performance of membrane on Pb(II) ion was analized by filtration of Pb(NO3)2 solution. Based on the swelling test and mechanical test, it can be concluded that chitosan-silica 3% has the best characteristics. The functional groups of chitosan-silica membrane 3% showed that there was a shift, a decrease or increase of wavenumber, and there was new functional groups found, indicated the functional group of silica in membrane. The chitosan-silica membrane 3% has capability to filter Pb(II) ion in solution with coefficient rejection is 26,84%. The analysis SEM generally showed that the membrane morphology of chitosan-silica looks tight and smooth surface.

Key words: chitosan-silica membrane, filtration, Pb(II) ion, coefficient of rejection