KARAKTERISASI GRAPHENE ARANG AMPAS TEBU BERBASIS X-RD DAN TEM

  • LADHITA TRIPRAYOGA SUTAYASA

Abstract

Abstrak. Telah dilakukan penelitian mengenai pembuatan dan karakterisasi graphene dari arang ampas tebu menggunakan metode kimia modifikasi Improved Graphene Oxide (IGO). Pada penelitian ini menggunakan material awal berupa ampas tebu hasil penggilingan pabrik gula Candi Sidoarjo serta digunakan material pembanding berupa grafit alam. Pada uji kristalinitas X-RD menunjukkan puncak 2θ pada 26,343o dengan nilai d-spacing 0,338050 nm serta ukuran kristal sebesar 15,41 nm. Hasil uji morfologi TEM menunjukkan adanya few-layer graphene (FLG) serta bagian layer graphene yang sangat tipis dan transparan hingga penanda mikron pada ukuran 20 nm. Pada pengujian menggunakan. Pada material pembanding berupa grafit alam, produk graphene yang dihasilkan juga menunjukkan hasil yang serupa pada pengujian instrumen yang sama. Produk graphene dari arang ampas tebu dan grafit alam menunjukkan adanya few-layer graphene dalam produk yang dihasilkan.

Kata kunci: modifikasi IGO, graphene, few-layer graphene

Abstract. The research has been done to making and characterization of graphene from bagasse charcoal using chemical modification methods of Improved Graphene Oxide (IGO). In this research, using a starting material from bagasse, the grinding results of Candi Sidoarjo sugar mill, and use reference material from natural graphite. The crystallinity X-RD test results showed peaks at 2θ 26,343o with d-spacing value of 0.338050 nm and the crystal size of 15.41 nm. TEM morphology test results indicate the presence of few-layer graphene (FLG) as well as part of the graphene layer is very thin and transparent to the marker microns in size 20 nm. Meanwhile the reference material from natural graphite, graphene product from graphite also showed similar results in testing the same instrument. The graphene product from bagasse charcoal and natural graphite showed few-layer graphene in the resulting product.

Key words: modification of IGO, graphene, few-layer graphene

Published
2016-11-29
Abstract Views: 173
PDF Downloads: 601