AKTIVITAS SELF CLEANING PADA KAIN KATUN TERLAPISI TiO2 DENGAN BINDER ASAM OKSALAT SELF CLEANING ACTIVITIES ON COTTON FABRIC COATED TiO2 WITH BINDER OXALIC ACID

  • ANGGA DWI YUNIANTO
  • DINA KARTIKA MAHARANI

Abstract

Abstrak. Tujuan penelitian ini untuk mengetahui aktivitas self cleaning pada kain katun yang terlapisi TiO2 dengan binder asam oksalat. Kain katun dilapisi binder asam oksalat dengan variasi konsentrasi 25%, 30%, 35%, dan 40%. Kain yang telah terlapisi binder asam oksalat kemudian dilapisi dengan TiO2 menggunakan metode pad-dry-cure. Karakterisasi kain terlapisi TiO2 dan binder asam oksalat menggunakan SEM-EDX serta pengujian aktivitas self cleaning menggunakan uji ketuaan warna. Pengujian aktivitas self cleaning terbaik dihasilkan pada kain terlapisi TiO2 menggunakan binder asam oksalat 25% dengan aktivitas self cleaning 10,7. Hasil tersebut juga didukung dengan data SEM dimana ditunjukan morfologi kain yang terlapisi partikel Ti yang seragam dan hasil EDX menunjukkan lebih banyak Ti yang teremban pada kain dari pada tanpa menggunakan binder.

Kata Kunci : self cleaning, binder asam oksalat, TiO2

Abstract. The purpose of this research is to know self cleaning activity on TiO2 coated cotton fabric with oxalic acid binder. Cotton fabric coated oxalic acid binder with variation concentration 25%, 30%, 35%, and 40%. The coated fabric of the oxalic acid binder is then coated with TiO2 using a pad- dry-cure method. Characterization of TiO2 coated fabrics and oxalic acid binder using SEM-EDX as well as self cleaning activity test using color aging test. Testing of the best self-cleaning activity produced on TiO2 coated fabrics using 25% oxalic acid binder with self-cleaning activity 10.7. The results are also supported by SEM data which shows the morphology of fabric coated with good Ti particles and EDX results show more Ti bonded to the fabric than without binders.

Keywords: self cleaning, binder oxalic acid, TiO2