UJI AKTIVITAS PEREDAMAN RADIKAL BEBAS NANOPARTIKEL EMAS DENGAN BERBAGAI KONSENTRASI SEBAGAI MATERIAL ANTIAGING DALAM KOSMETIK (FREE RADICAL SCAVENGING of ACTIVITY TEST of GOLD NANOPARTICLES WITH VARIOUS CONCENTRATIONS as ANTIAGING MATERIAL in COSMETICS)

  • ENDAH MUSFIROH Jurusan Kimia, FMIPA, Universitas Negeri Surabaya

Abstract

Abstrak. Telah dilakukan penelitian tentang uji aktivitas peredaman radikal bebas nanopartikel emas dengan berbagai konsentrasi sebagai material antiaging dalam kosmetik. Tujuan dari penelitian ini untuk mengetahui pengaruh konsentrasi nanopartikel emas terhadap aktivitas peredaman radikal bebas (DPPH). Konsentrasi nanopartikel emas yang digunakan antara lain 5 ppm, 10 ppm, 15 ppm, 20 ppm, 25 ppm, dan 30 ppm. Untuk menguji aktivitas peredaman radikal bebas digunakan spektrofotometer Uv-Vis. Sintesis nanopartikel emas dilakukan melalui beberapa tahap, yaitu pembuatan larutan induk HAuCl4, mereduksi larutan HauCl4 melalui proses buttom-up yaitu dengan cara mereduksi ion logam (Au3+) menjadi logam yang tidak bermuatan (Au0) yang ditandai dengan perubahan warna dari larutan emas yang berwarna kuning menjadi merah anggur. Hasil penelitian menunjukkan bahwa persen peredaman nanopartikel emas dengan variasi konsentrasi 5 ppm; 10 ppm; 15 ppm; 20 ppm; 25 ppm; dan 30 ppm yaitu 26,405 %; 43,782%; 27,762%; 27,257%; 60,647%; dan 61,158%. Hasil ini menunjukkan bahwa semakin besar konsentrasi maka semakin besar persen peredaman. Namun pada penelitian ini belum terlihat konsentrasi optimal peredaman karena variasi yang dilakukan terbatas sampai pada 30 ppm.

 

Kata kunci : uji aktivitas peredaman radikal bebas, nanopartikel emas, DPPH.

Abstract. It has been done research about free radical of scavenging activity test of gold nanoparticles with various concentrations as antiaging material in cosmetics. The purpose of the study were determined the effect of concentration of gold nanoparticles on the free radical (DPPH) scavenging activity. Concentration of gold nanoparticles used were 5 ppm, 10 ppm, 15 ppm, 20 ppm, 25 ppm and 30 ppm. To test the free radical of scavenging activity used UV-Vis spectrophotometer. Synthesis of gold nanoparticles through several stages, that was aqueous solution  HAuCl4, reducing the solution HauCl4 through the buttom-up is by reducing the metal ions (Au3+) into the metal which was not charged (Au0) indicated by color change from yellow of gold solution to red wine. The results showed that the scavenging percent of gold nanoparticles by varying the concentration of 5 ppm, 10 ppm, 15 ppm: 20 ppm, 25 ppm, and 30 ppm which is 26,405 %; 43,782%; 27,762%; 27,257%; 60,647%; and 61,158%. These results indicated that greater the concentration the greater the scavenging percent. But in this study have not seen the optimal concentration of scavenging due to the limited variation performed at 30 ppm.

Key words : free radical of scavenging activity test, gold nanoparticles, DPPH