SINTESIS DAN KARAKTERISASI PADATAN SILIKA-ALUMINA DENGAN VARIASI SUHU KALSINASI SEBAGAI PENDUKUNG KATALIS CAMPURAN OKSIDA LOGAM Cu/Zn SYNTHESIS AND CARACTERIZATION OF SILICA-ALUMINA WITH CALCINATION TEMPERATURE VARIATION AS MATRIX Cu/Zn MIXED METAL OXIDE CATALYST

  • MUHAMMAD NUR KHOLILUR ROHMAN

Abstract

Abstrak. Telah dilakukan sintesis dan karakterisasi padatan silika-alumina sebagai pendukung katalis campuran oksida logam Cu/Zn untuk konversi gas buang CO. Padatan silika-alumina dipreparasi dengan metode sol-gel dan dikalsinasi pada suhu 550, 650 dan 750 oC. Katalis campuran oksida logam Cu/Zn/SA disintesis dengan metode impregnasi. Padatan pendukung hasil sintesis dikarakterisasi dengan XRD dan FTIR serta katalis Cu/Zn/SA dianalisa dengan XRD, FTIR, dan BET. Hasil difraksi sinar-X padatan pendukung menunjukkan SA 750 memiliki kristalinitas yang lebih baik dibandingkan SA 550 dan SA 650. Analisa gugus fungsional menunjukkan silika-alumina didominasi oleh gugu-gugus OH, Si-OH dan Al-OH. Hasil difraksi sinar-X ketiga padatan silika-alumina setelah impregnasi menunjukkan puncak utama karakteristik CuO pada 2θ 35,5o dan 38,7o serta puncak karakteristik ZnO pada 2θ 68o. Hasil analisa dengan metode BET menunjukkan luas permukaan spesifik padatan katalis Cu/Zn dengan pendukung silika-alumina 550, 650, dan 750 berturut-turut adalah 136,070; 136,713; dan 104,819 m2/g. Hasil analisa dengan FTIR pada katalis Cu/Zn/SA750 menunjukkan pita vibrasi ulur oksida logam M-O yang sangat dominan, yang berarti bahwa oksida logam CuO dan ZnO yang terbentuk pada padatan silika-alumina terdapat dalam jumlah yang tinggi. Kata kunci : Sintesis, silika-alumina, oksida logam Abstract. Synthesis and characterization of a silica-alumina as matrix of Cu/Zn mixed metal oxide catalyst for the conversion of CO exhaust gases has been done. The solid silica-alumina was prepared by sol-gel method and calcined at 550, 650, and 750 oC. The Cu/Zn/SA mixed metal oxide catalyst was synthesized by impregnation method. The solid support synthesis results were characterized by XRD and FTIR, and the Cu/Zn/SA catalyst was analyzed by XRD, FTIR, and BET. The results of X-ray diffraction showed solid support SA 750 has better crystallinity than the SA 550 and SA 650. The functional group analysis showed silica-alumina was dominated by -OH, Si-OH and Al–OH groups. The results of X-ray diffraction of silica-alumina solid third after impregnation showed a major peak characteristic of CuO at 2θ 35,5o and 38,7o and the peak chaaracteristic of ZnO at 2θ 68o. The results of the analysis with BET method showed that specific surface area of the catalyst Cu/Zn with matrix silica-alumina 550, 650, and 750 were 136.070; 136.713; and 104.819 m2/g, respectively. The results of the FTIR analysis on a mixed metal oxides Cu/Zn/SA750 showed stretching vibration bands of metal oxide M-O has much dominant, which means that the metal oxides of CuO and ZnO are formed on silica-alumina solids present in high quantities.
Keywords: Synthesis, silica-alumina, metal oxide

Published
2014-08-04
Abstract View: 4
PDF Download: 11