PEMANFAATAN ARANG AKTIF KULIT BUAH COKLAT (Theobroma cacao L.) SEBAGAI ADSORBEN LOGAM BERAT Cd (II) DALAM PELARUT AIR (UTILIZATION OF (Theobroma cacao. L) CACAO SKIN FOR ACTIVATED CARBON AS ADSORBENT CADMIUM (II) IN SOLUTION)

  • Yana Fuad Masitoh Department of Chemistry, Faculty of Mathematics and Natural sciences State University of Surabaya Jl. Ketintang Surabaya (60231), Telp. 031-8298761
  • Maria Monica Sianita Department of Chemistry, Faculty of Mathematics and Natural sciences State University of Surabaya Jl. Ketintang Surabaya (60231), Telp. 031-8298761

Abstract

Abstrak. Tujuan dari penelitian ini adalah untuk mengetahui karakteristik arang aktif kulit buah coklat
yang digunakan sebagai adsorben Cd (II), waktu kontak optimum, dan massa adsorben maksimum yang
diperlukan untuk mengadsorpsi Cd (II). Metode yang digunakan berdasarkan metode isoterm Langmuir
dengan menggunakan Spektroskopi Serapan Atom (SSA). Preparasi arang aktif dari kulit buah coklat
dilakukan dengan cara karbonisasi pada temperatur 500oC. Pengaktifan arang dilakukan dengan
menggunakan ZnCl2 9% selama 16 jam pada pemanasan 300oC dan 600oC. Adsorpsi dilakukan dengan
waktu kontak 20, 40, 60, 80, dan 100 menit dan massa adsorben 1, 2, 3, 4, 5, 6, 8 dan 10 gr. Hasil arang
aktif yang terbaik diperoleh pada suhu 600oC dengan kadar air 5,863%, kadar abu 9,863%, zat yang
mudah menguap 8,356%, dan daya serap terhadap iod 816,583 mg/g. Kapasitas adsorpsi arang aktif
terhadap Cd (II) adalah 94,075% dengan massa adsorben 6 gram dan waktu kontak optimum 60 menit.
Kata kunci : adsorpsi, arang aktif, kulit buah coklat, logam kadmium(II)
Abstract. The purpose of this research was to determine the characteristics of activated carbon from
cacao skin used as adsorbent of Cd (II), the optimum contact time, and the maximum mass of adsorbent
required to adsorb the heavy metal Cd (II). The method used is based on the Langmuir isotherm method
and using Atomic Absorption Spectroscopy (AAS). Preparation of activated carbon from cacao skin was
conducted by carbonization at 500oC. Activation of carbon was conducted using ZnCl2 9% for 16 hours at
300oC and 600oC. The Adsorption was conducted with contact time using of 20, 40, 60, 80, and 100
minutes and adsorbent mass of 1, 2, 3, 4, 5, 6, 8 and 10 gr. The best result of activated carbon was obtain
at 600oC with water content 5,863%, ash content 9,863%, volatile substances 8,356%, and the absorption
of iodine 816.583 mg/g. The adsorption capacity of activated carbon of Cd (II) was 94,075% using 6
grams of adsorbent mass and optimum contact time of 60 minutes.
Keywords : adsorption, activated carbon, (Theobroma cacao. L) cacao skin , cadmium(II)